Lieu d'origine : Tianjin, Chine (continent)
forme : bloquer
matériel : teneur en SiO2 alumine bloc
(%): 50 % ~ 65 %
teneur en Al2O3 (%): teneur en MgO 75 %
(%): teneur en CaO 90 % min
(%): 0,01
période réfractaire (degré): 1770°< 2000°
CrO Content (%): 0.1~0.3%
SiC Content (%): 1.2-1.4
Packaging Details: Standard seaport pakage
Delivery Detail: According to actual requirements.
1.Alumina carbon bricks and Alumina Zirconia carbon slide gate plate
Material: tabular alumina, carbonaceous material and zirconia-containing material.
Additive: high performance antioxidants.
Bonder: phenolic resin
Advantage: high strength, good erosion resistance, thermal shock resistance and good stability.
Mainly use: large and middle size ladles.
- MgO and MgO-spinel slide gate plate
Material: high –purity and high density fused magnesia, graphite or sintered magnesium aluminate spinel.
Additive: Antioxidant
Binder: Phenolic resin
Use: High quality steel casting 2000°=""
cro="" content="" (%):="" 0.1~0.3%=""
sic="" content="" (%):="" 1.2-1.4
packaging="" details:="" standard="" seaport="" pakage
delivery="" detail:="" according="" to="" actual="" requirements.
1.alumina="" carbon="" bricks="" and="" alumina="" zirconia="" carbon="" slide="" gate="" plate
material:="" tabular="" alumina,="" carbonaceous="" material="" and="" zirconia-containing="" material.
additive:="" high="" performance="" antioxidants.
bonder:="" phenolic="" resin
advantage:="" high="" strength,="" good="" erosion="" resistance,="" thermal="" shock="" resistance="" and="" good="" stability.
mainly="" use:="" large="" and="" middle="" size="" ladles.
2.="" mgo="" and="" mgo-spinel="" slide="" gate="" plate
material:="" high="" –purity="" and="" high="" density="" fused="" magnesia,="" graphite="" or="" sintered="" magnesium="" aluminate="" spinel.
additive:="" antioxidant
binder:="" phenolic="" resin
use:="" high="" quality="" steel="">