ALANITE GA Series Thermostable Ink
Ⅰ、Description
ALANITE GA series inks, which prepared with special mixed-resin, extra fine fillers and pigments, and so on, are not only feeling fine and smooth, but also of good leveling and printability. The after-treatment on the presswork is feasible, such as punching, drilling, cutting, etc. Excellent adhesion. Chemical resistance, boiling and alcohol resistant. High gloss. Light fastness.
Ⅱ、Recommended Application
◆ Recommended substrate: Metal plates. Glass. Stainless Steel. Chinaware. Porcelain enamel. Etc.
Ⅲ、Proposed Operation
Prepare: To clean the surface with ALATIVE SC5 treater and make sure non-dust, non-grease. To dilute the ink with 3-20% ALATIVE SR6 thinner（In order to regulate the drying rate of ink ,please make use of ALATIVE RR6 dry retarder or ALATIVE SF3 dry accelerant）.
Mesh count: 70T to 180T
Drying: Heat cure at 200℃-650℃in about 30 minutes.
Cleaning: To remove the stain and bad print with ALATIVE SC6 remover before heat cure, and to clear the screen plate with ALATIVE CC6 cleaner.
Ⅳ、Color & Packaging
Color: More than 20 kinds of colors for selection and with professional mixed-color service.
Packaging: 5kg/barrel, 20kg/barrel
Ⅴ、Annotation
1, Test Condition (ALANITE GA Series Inks)
Substrate Printing Inks Remark
Glass ALANITE GA-223 300OC heat cure in 40 minute,
Then more than three hour later, about 25OC
2, Test Result of the Film (ALANITE GA Series Inks)
Item Test Method Result
Adhesive Force Cross cut, Peeling test with adhesive tape 100/100 Pass
Rigidity Angle 45O, 1200g, Pencil hardness 2H-3H
Water Resistance Water immersion in five weeks No Effect
Acid Resistance Immersion 30% H2SO4 aqueous solution in 10 hours No Effect
Alcohol Resistance 1200g, Back and forth wipe 100 times with alcohol cloth No Effect
Xylene Resistance 1000g, Back and forth wipe 50 times with xylene cloth No Effect
Gasoline Resistance 1000g, Back and forth wipe 50 times with gasoline cloth No Effect
Abrasion Resistance 500g, Back and forth scrape 500 times with eraser No Effect
Weatherability Back printing, Accelerated exposing aging test 800 hr.